Polyester film for sealing backside of solar cell

ABSTRACT

The present invention provides a polyester film for sealing the backside of solar cell having excellent light reflectivity and durability and good electric insulation. A polyester film for sealing the backside of solar cell having a light reflectance at 550 nm wavelength of 50% or more and containing 3 to 50% by mass of inorganic fine particles, characterized in that acid value of the film is 1 to 30 eq/ton and limiting viscosity of the film is 0.60 to 0.80 dL/g.

TECHNICAL FIELD OF THE INVENTION

The present invention relates to a polyester film for sealing thebackside of solar cell having excellent light reflectivity anddurability and good electric insulation.

BACKGROUND ART

Recently, solar cells are receiving public attention as a clean energysource of the next generation. In a solar cell module, a component suchas a sheet for sealing the backside of solar cell which seals thebackside of solar cell module is used and a substrate film is used forthe component as such. Since a solar cell used in outside is used for along period of time, the component therefor is to be also durable undernatural environment. As to the component such as a substrate film forsealing the backside of solar cell, there is used fluorine film,polyethylene film or polyester film (cf. Patent Documents 1 and 2). Asto a sheet for sealing the backside of solar cell, there is proposed awhite sheet for sealing the backside of solar cell in order to enhancethe photoelectric conversion efficiency of the solar cell device (cf.Patent Documents 3 to 7).

Further, for improving the properties of the solar cell system as awhole, there has been a strong demand for setting the system voltagehigh. Therefore, there has been an increasing demand for the electricinsulation property to the sheet for sealing the backside of solar celland there have been proposals for a sheet for sealing the backside ofsolar cell compatible with the system voltage of 1,000 V (cf. PatentDocuments 8 and 9).

Furthermore, as mentioned in the above Patent Documents, a polyesterfilm of high whiteness degree has been used for reflecting the sunlightand for enhancing the generation efficiency by the solar cell device. Inorder to prepare a polyester film of high whiteness degree, it isnecessary to add a lot of particles to the polyester substrate. At thattime, many thermal hystereses are added due to the fact that a rawmaterial where two or more materials are preliminarily mixed or thatmelting time is made long even in the usual extruding step so as to makethe dispersibility and mixing state thereof good. Therefore, thepolyester resin is hydrolyzed and is apt to be deteriorated wherebythere has been a problem of poor durability when it is used under hightemperature and humidity. Accordingly, it has been common up to nowthat, as mentioned in the Patent Document 7, a white layer and a layerhaving durability are prepared as separate functional layers followed bylaminating them and it has been difficult to satisfy both highreflectivity and durability by a single layer.

Still further, in recent years, the mode for use of solar cell isdeveloping from just placing on a roof to a large-scale photovoltanicgenerator in desert regions, etc. and a solar cell module has beenbecoming to large size and high output of power. At that time, manysolar cell devices are aligned in a sheet of solar cell module. Whenunbalanced generation characteristic happens for each of the solar celldevices, load is focused to a solar cell device having low generationcharacteristic whereby the temperature of such a solar cell device partbecomes particularly high. In a solar cell module where such a hot spotis resulted, the material around the hot spot is exposed to hightemperature and, as a result, that causes deterioration of the resinsuch as sealing resin or backside protecting membrane or inferioritysuch as detachment.

PRIOR ART DOCUMENTS Patent Documents

-   Patent Document 1: Japanese Patent Application Laid-Open (JP-A) No.    261085/99-   Patent Document 2: Japanese Patent Application Laid-Open (JP-A) No.    2000-114565-   Patent Document 3: Japanese Patent Application Laid-Open (JP-A) No.    2004-247390-   Patent Document 4: Japanese Patent Application Laid-Open (JP-A) No.    2002-134771-   Patent Document 5: Japanese Patent Application Laid-Open (JP-A) No.    2007-208179-   Patent Document 6: Japanese Patent Application Laid-Open (JP-A) No.    2008-85270-   Patent Document 7: Japanese Patent Application Laid-Open (JP-A) No.    2008-4839-   Patent Document 8: Japanese Patent Application Laid-Open (JP-A) No.    2006-253264-   Patent Document 9: Japanese Patent Application Laid-Open (JP-A) No.    2008-166338

DISCLOSURE OF THE INVENTION Problem that the Invention is to Solve

The present invention has been created in view of the above problems inthe prior art and its object is to provide a polyester film for sealingthe backside of solar cell having both high reflectivity and durabilityand achieving excellent electric insulation. Further object of thepresent invention is to provide a polyester film for sealing thebackside of solar cell which contributes in uniform generatingcharacteristic in the module.

Means for Solving the Problem

The present inventors have conducted intensive investigation forachieving the above objects and, as a result, they have found that bothwhiteness degree and resistance to hydrolysis can be made compatiblewith each other when acid value and limiting viscosity of the film arecontrolled within a specific range whereupon the present invention hasbeen accomplished.

Thus, the present invention adopts the constitutions of the following(1) to (10):

(1) A polyester film for sealing the backside of solar cell having alight reflectance at 550 nm wavelength of 50% or more and containing 3to 50% by mass of inorganic fine particles, characterized in that acidvalue of the film is 1 to 30 eq/ton and limiting viscosity of the filmis 0.60 to 0.80 dL/g.

(2) The polyester film for sealing the backside of solar cell accordingto (1), wherein in-face variation of the light reflectance to the meanvalue of the light reflectance is 5% or less.

(3) The polyester film for sealing the backside of solar cell accordingto (1) or (2), wherein the inorganic fine particles are titanium oxideof a rutile type.

(4) The polyester film for sealing the backside of solar cell accordingto any of (1) to (3), wherein the thickness is 30 to 300 μm.

(5) The polyester film for sealing the backside of solar cell accordingto any of (1) to (4), wherein the partial discharge voltage is 550 V orhigher.

(6) The polyester film for sealing the backside of solar cell accordingto any of (1) to (5), wherein the layered numbers of cavities existingin the thickness direction of the film is 5 or more and the density oflayered numbers of cavities defined by the following formula is within arange of 0.1 to 7/μm:

Density of layered numbers of cavities (numbers/μm)=[Layered numbers ofcavities in the thickness direction of film]/[Thickness of film (μm)]

(7) The polyester film for sealing the backside of solar cell accordingto any of (1) to (6), wherein an applied layer is provided at least onone side of the film and a urethane resin where an aliphaticpolycarbonate polyol is a constituting component is a main component ofthe applied layer.

(8) The polyester film for sealing the backside of solar cell accordingto any of (1) to (7), wherein the film is used on the face of a sidecontacting an encapsulation foil for a solar cell module and/or on theoutermost face of a solar cell module.

(9) The polyester film for sealing the backside of solar cell accordingto any of (1) to (8), wherein the film is obtained by preparing a masterbatch comprising a polyester resin and inorganic fine particles;subjecting the master batch to solid-phase polymerization and; afterthat, pouring a polyester resin containing no inorganic fine particlesand the master batch into an extruder and melt extruding the mixture.

(10) A solar cell module which is characterized in containing thepolyester film for sealing the backside of solar cell mentioned in anyof (1) to (8), an encapsulation foil layer being adjacent to thepolyester film and a solar cell device embedded in the encapsulationfoil layer.

Advantages of the Invention

The polyester film for sealing the backside of solar cell of the presentinvention has both high light reflectivity and durability. Moreover,even when it is thin, the film has good electric insulation and also hasuniform light reflectivity characteristic in a module. Accordingly, whenthe polyester film for sealing the backside of solar cell of the presentinvention is used, a solar cell module having excellent durability, lowcost and light weight can be provided.

BEST MODE FOR CARRYING OUT THE INVENTION

The polyester used for the film of the present invention is a polyesterproduced by polycondensation of an aromatic dicarboxylic acid such asterephthalic acid, isophthalic acid or naphthalenedicarboxylic acid oran ester thereof with a glycol such as ethylene glycol, diethyleneglycol, 1,4-butanediol or neopentyl glycol. Instead of a method by adirection reaction of aromatic dicarboxylic acid with glycol, thepolyester can be produced by a method where polycondensation isconducted after an ester interchange of alkyl ester of aromaticdicarboxylic acid with glycol, by a method where diglycol ester ofaromatic dicarboxylic acid is subjected to polycondensation, etc.Typical examples of the polyester as such include polyethyleneterephthalate, polyethylene butylene terephthalate andpolyethylene-2,6-naphthalate. The polyester may be either a homopolymeror a product copolymerized with a third component. In the presentinvention, a preferred polyester is the one having 70 molar % or more,preferably 80 molar % or more, and more preferably 90 molar % or more ofethylene terephthalate unit, butylene terephthalate unit orethylene-2,6-naphthalate unit.

As a catalyst for polycondensation of a polyester, there may be used acatalyst containing antimony compound, titanium compound, germaniumcompound, tin compound, aluminum and/or a compound thereof and aphosphorus compound having an aromatic group in a molecule, a catalystcontaining aluminum salt of phosphor compound, etc. The catalysts assuch may be coexisted in appropriate amounts within such an extent thatno problem is resulted thereby in terms of characteristic,processability and color tone of the polyester.

It is also possible to further enhance the thermostability of apolyester by such a means that, after polymerization of a polyester, acatalyst is removed from the resulting polyester or a catalyst isinactivated by addition of a phosphorus compound or the like.

During the polymerization of polyester, dialkylene glycol isby-produced. When exposed to high temperature for a long period as asolar cell material, there is a case where heat resistance lowers by theinfluence of dialkylene glycol. When an explanation is done takingdiethylene glycol as a typical dialkylene glycol, amount of diethyleneglycol is preferred to be 2.3 molar % or less. It is more preferred tobe 2.0 molar % or less, and it is further preferred to be 1.8 molar % orless. When amount of diethylene glycol is made within the above range,thermostability can be enhanced and an increase in the concentration ofcarboxyl terminal (a rise in acid value) due to the decomposition upondrying or molding can be made far less. The less the amount ofdiethylene glycol, the better but diethylene glycol is produced as aby-product upon esterifying reaction of terephthalic acid or upon esterinterchange reaction of dimethyl terephthalate in the production ofpolyester and, practically, its lower limit is 1.0 molar % or, further,1.2 molar %.

Depending upon the object of use, the polyester may contain one or moreadditive (s) such as fluorescent whitener, ultraviolet preventer,infrared absorbing dye, thermostabilizer, surfactant or antioxidant. Asan antioxidant, that of an aromatic amine or phenol type can be used. Asa stabilizer, that of a phosphorus type (e.g., phosphoric acid andphosphate), a sulfur type or an amine type can be used.

When exposed outside for long time as a solar cell component, there maybe the case where molecular weight of polyester lowers due todeteriorative decomposition, resulting in lowering of film strength.Therefore, it is necessary that, in the polyester film of the presentinvention, limiting viscosity of the film is 0.60 to 0.80 dL/g forimparting the durability as a solar cell component. When the limitingviscosity of the film is less than the above lower limit, it isdifficult to achieve a long-term resistance to hydrolysis as a solarcell component while, when it is more than the above upper limit,breaking upon film manufacture is apt to happen. In addition, a rise intemperature takes place due to heat generation in a melt extruder and itbecomes difficult to uniformly mix the inorganic fine particles in thepolyester. Lower limit of the above limiting viscosity is preferably0.63 dL/g, more preferably 0.64 dL/g, and further preferably 0.65 dL/g.Upper limit of the above limiting viscosity is preferably 0.79 dL/g andmore preferably 0.78 dL/g.

A carboxyl terminal of the polyester has an action of promoting thehydrolysis due to its self-catalytic action. Therefore, for achieving ahigh resistance to hydrolysis as a solar cell component, it is necessarythat acid value of the film of the present invention is within a rangeof 1 to 30 eq/ton. The above acid value is preferred to be 3 to 30eq/ton and more preferred to be 5 to 30 eq/ton. When the acid value ismore than the above range, resistance to hydrolysis lowers, durabilityas a solar cell component cannot be achieved and deterioration in earlystage is apt to happen. Acid value of the film or the polyester can bemeasured by a titration method or by an NMR method which will bementioned later.

For making the acid value of the polyester film within the above range,it is preferred that acid value of the polyester tip used as a materialresin is made less than 25 eq/ton. The acid value of the polyester tipused is more preferred to be less than 20 eq/ton, further preferred tobe less than 13 eq/ton, furthermore preferred to be less than 10 eq/ton,particularly preferred to be less than 8 eq/ton, more particularlypreferred to be less than 5 eq/ton. Making the acid value of thepolyester chip within the above range can be conducted by appropriatelyselecting the polymerization condition of the resin. For example, it canbe conducted by appropriately setting the factor of the manufacturingapparatus such as the structure of the esterifying reaction apparatus;the esterifying reaction condition such as the composition ratio ofdicarboxylic acid to glycol to be supplied to an esterifying reactor,temperature for the esterifying reaction, pressure for the esterifyingreaction or time for the esterifying reaction; or the condition forsolid-phase polymerization. Further, as will be mentioned later, it ispreferred to control the moisture content of the polyester chip or tocontrol the resin temperature in the melting step. It is also possiblethat a carboxyl terminal of the polyester is sequestered by an epoxycompound, a carbodiimide compound, etc. Although it is preferred thatthe acid value of the polyester film is small, its lower limit has beenbelieved to be 0.5 eq/ton in view of the productivity.

For utilizing the light effectively and enhancing the photoelectricconversion efficiency of the solar cell device, the polyester film ofthe present invention has a high light reflectance. In the polyesterfilm of the present invention, the light reflectance at 550 nmwavelength is 50% or more, preferably 60% or more and further preferably70% or more. Since the polyester film of the present invention wellscatters the light, quantity of light returning to the solar cell deviceincreases and it is advantageous for being used in a thin-membrane solarcell. With regard to the above range of light reflectance, although itis sufficient when its measured value in any side of the film satisfiesthe range, the case where the values satisfy the above range in bothsides of the film is preferred since freedom of processing increasesthereby.

Further, it is preferred that degree of whiteness of the polyester filmof the present invention is 50 or more, more preferred to be 60 or more,and further preferred to be 80 or more.

For controlling the light reflectance to the above range, the polyesterfilm of the present invention contains 3 to 50% by mass, preferably 3.50to 25% by mass, of inorganic fine particles to the total mass of thefilm. When the amount of the inorganic fine particles is less than 3% bymass, it is difficult to make the light reflectance at 550 nm wavelength50% or more. When the amount is more than 50% by mass, weight of thefilm becomes too big, which makes the handling in a processing, etc.difficult.

Average particle size of the inorganic fine particles is preferred to be0.1 to 3 μm and more preferred to be 0.5 to 2.5 μm. When averageparticle size of the inorganic fine particles is less than 0.1 μm, theremay be the case where light reflectivity characteristic cannot beadvantageously enhanced by a light scattering effect. When averageparticle size of the inorganic fine particles is more than 3 μm, theremay be the case where breakage of the film is resulted or manufacture ofthe film cannot be advantageously carried out.

In the present invention, average particle size of the inorganic fineparticles is determined by an electron microscopic method. To be morespecific, the following method is conducted. Thus the fine particles areobserved under a scanning electron microscope and the pictures are takenthereby appropriately changing the multiplications depending upon theparticle size, and the taken pictures are enlarged and copied. As to atleast 100 fine particles selected randomly, the outer circumference ofeach particle is traced. Diameters corresponding to the circles of theparticles are measured from the traced images using an image analyzerand the mean value thereof is adopted as an average particle size.

Although the inorganic fine particles to be contained in the polyesterfilm of the present invention are not particularly limited, examplesthereof include silica, kaolinite, talc, calcium carbonate, zeolite,alumina, barium sulfate, carbon black, zinc oxide, titanium oxide andzinc sulfate. In view of light reflectivity and productivity, whitepigment or, in other words, titanium oxide or barium sulfate ispreferred, and titanium oxide is more preferred.

Since solar cell in outside is irradiated with sunlight for long time,durability against deterioration by light is demanded. With regard tosuch a respect, it is preferred to add particles of titanium dioxidemainly comprising a rutile type as the inorganic fine particles to beused for the film of the present invention. In titanium oxide, twocrystalline forms of rutile type and anatase type have been mainlyknown. There are such characteristic properties that anatase type has avery big spectral reflectance for ultraviolet ray and that rutile typehas a big absorption rate for ultraviolet ray (small spectralreflectance). When an ultraviolet absorbing property of rutile type isutilized paying the attention to such a difference in spectralcharacteristic in the crystal form of titanium dioxide, resistance tolight can be advantageously improved. As a result thereof, the film ofthe present invention has excellent film durability under irradiation oflight even when other ultraviolet absorber is not substantially added.Therefore, problems such as pollution and lowering of close adhesion bybleeding out of ultraviolet absorber hardly take place.

The term “main component” used herein means that the amount of titaniumdioxide of rutile type in all titanium dioxide particles is more than50% by mass. Amount of titanium dioxide of anatase type in all titaniumdioxide particles is preferred to be 10% by mass or less. It is morepreferred to be 5% by mass or less and further preferred to be 0% bymass. When the amount of titanium dioxide of anatase type is more thanthe above upper limit, the amount of titanium dioxide of rutile type inall titanium dioxide particles becomes small whereby the ultravioletabsorbing property becomes insufficient and, besides that, sincetitanium dioxide of anatase type has a strong photocatalytic action,resistance to light tends to lower by such an action as well. Titaniumdioxide of rutile type and that of anatase type can be discriminated byX-ray structure diffraction or spectral absorption characteristic.Incidentally, surfaces of titanium oxide particles of rutile type may besubjected to an inorganic treatment using, for example, alumina orsilica or may be subjected to an organic treatment using, for example,silicone or alcohol.

According to the above-mentioned constitution, the film of the presentinvention can achieve excellent durability even under irradiation oflight. To be more specific, in the film of the present invention, theretention rate of breaking elongation can be 35% or more, further it canbe 40% or more, when UV irradiation is done for 100 hours withirradiation intensity of 100 mW/cm² at 63° C. and 50% RH. Since the filmof the present invention suppresses photodecomposition and deteriorationas such under irradiation of light, it is advantageous as a backsidesealing sheet for solar cell used outside.

Addition of the inorganic fine particles into the film can be carriedout by the known method and it is preferred to conduct by a master batchmethod (MB method) where polyester resin and fine particles arepreviously mixed using an extruder. According to such a method,inorganic fine particles can be advantageously dispersed in thepolyester and uneven light reflectivity in the film surface can besuppressed.

In preparing a master batch, a rise in acid value may happen due tohydrolysis of the polyester. Therefore, it is preferred to control themoisture in preparing a master batch. The polyester resin and inorganicfine particles are poured into an extruder and, together with removal ofmoisture and air therefrom, a master batch can be prepared. Morepreferably, when a master batch is prepared using a polyester resinwhich was previously dried even only a little, a rise in acid value ofthe polyester can be suppressed. In that case, there will be a methodwhere extrusion is conducted together with deaeration, a method whereextrusion is conducted without deaeration using a well-dried polyesterresin or the like.

In preparing a master batch, it is preferred that the polyester resin tobe poured is previously dried to reduce the moisture content therein. Asto a drying condition, it is preferred to dry at 100 to 200° C., morepreferably 120 to 180° C., for 1 hour or longer, more preferably for 3hours or longer and further preferably 6 hours or longer. At that time,drying is conducted sufficiently so as to make the moisture content ofthe polyester resin preferably 50 ppm or less and more preferably 30 ppmor less. There is no particular limitation for a method of previousmixing but either a method by batch or a method using a uniaxial,biaxial or higher axial kneading extruder may be used. In preparing amaster batch together with deaeration, it is preferred that thepolyester resin is melted at the temperature of 250 to 300° C.,preferably 270 to 280° C., one or, preferably, two or more deaerationorifice (s) is/are formed in the preliminary kneader and a continuoussucking deaeration is conducted at 0.05 MPa or more, preferably 0.1 MPaor more, so as to maintain the reduced pressure in the mixer.

In view of suppressing the in-face variation of light reflectance of thefilm, the film of the present invention is preferred to be manufacturedadopting a master batch method. However, due to hysteresis of heat andshear during the preparing process of the master batch, there may be thecase where molecular weight (limiting viscosity) lowers from that of theoriginal polyester resin. Therefore, there may be the case where, evenwhen mixed with a polyester resin of high molecular weight, nopredetermined limiting viscosity as a film can be achieved whereby along-term durability as a solar cell lowers. Particularly whenconcentration of the inorganic fine particles in the film is made highfor achieving a good light reflectivity, the mixing rate of the masterbatch is also apt to become high. Therefore, for achieving apredetermined limiting viscosity as a film advantageously, it ispreferred that the master batch is further subjected to a solid-phasepolymerization. Up to now, it has been believed that application of asolid-phase polymerization treatment to a master batch containing manyparticles is to be avoided since it promotes the degree ofcrystallization of the polyester and lowers the dispersibility of theparticles. However, as a result of such a treatment, the acid value canbe advantageously reduced in spite of containing the particles of highconcentration whereby the high limiting viscosity can be maintained. Asa result thereof, compatibility of both excellent light reflectivity anddurability can be advantageously achieved.

Solid-phase polymerization of the master batch can be conducted using abatch-type apparatus or a continuous-type apparatus. Solid-phasepolymerization of the polyester can be carried out by a conventionallyknown method. For example, a preliminary crystallization is conducted ininert gas, in vacuo, in water vapor or in an inert gas atmospherecontaining water vapor at the temperature of 100 to 210° C. for 1 to 5hour (s) and then a solid-phase polymerization is conducted in an inertgas atmosphere or in vacuo at the temperature of 190 to 230° C. for to30 hour (s). As to the time of the solid-phase polymerization, it ispreferred to be conducted until reaching the predetermined limitingviscosity by measuring the limiting viscosity of the polyester by meansof sampling. Acid value of a master batch is controlled by the acidvalue of the polyester (prepolymer) to be subjected to the solid-phasepolymerization, by the conditions for adjusting the humidity of theprepolymer, by the conditions for the crystallization, by the conditionsfor the solid-phase polymerization, etc. Acid value of the polyester canbe made low by lowering the acid value of the prepolymer, by suppressingthe hydrolysis during the crystallizing step or a solid-phasepolymerization step by making the moisture amount to be impregnatedduring the humidity adjustment of the prepolymer, by enhancing theethylene glycol concentration in an inert gas stream used upon thesolid-phase polymerization, etc.

Limiting viscosity of the master batch after the solid-phasepolymerization prepared as such is preferred to be 0.68 to 0.90 dL/g andmore preferred to be 0.70 to 0.85 dL/g. Acid value is preferred to be 1to 25 eq/ton. Although the film of the present invention can be preparedby mixing a master batch comprising a polyester resin containinginorganic fine particles with a polyester resin containing no inorganicfine particle followed by pouring into an extruder and by elongating themelt-extruded sheet at least in one direction, it is preferred that amaster batch comprising a polyester resin containing inorganic fineparticles is subjected to a solid-phase polymerization and then mixedwith a polyester resin containing no inorganic fine particle. Since thecrystallinity highly proceeds in the polyester resin after thesolid-phase polymerization, no crystallizing peak (exothermic peak atnear 120° C. in the case of polyethylene terephthalate) is noted whenthe polyester is subjected to differential scanning calorimetry. It ispossible to judge thereby whether the treatment by a solid-phasepolymerization was carried out.

For a purpose that the film of the present invention maintains highdurability when used as a solar cell, it is preferred that the polyesterresin to be mixed with the master batch is also subjected to thesolid-phase polymerization as mentioned above. As a result thereof, afilm having predetermined limiting viscosity and acid value can beadvantageously prepared. Here, for making the in-face light reflectioncharacteristic of the film surface uniform, it is preferred that themaster batch chip and the polyester chip to be mixed therewith areuniformly mixed. In that case, when there is a difference between thelimiting viscosities of the master batch chip and the polyester chip tobe mixed therewith since both are highly crystallized, there may be thecase where difference in the melting and flowing behaviors is resultedbetween them whereby the dispersibility of fine particles in thepolyester resin lowers. Difference between the limiting viscosity of themaster batch and the limiting viscosity of the polyester resin to bemixed therewith is preferred to be 0.15 dL/g or less, more preferred tobe 0.10 dL/g or less, and further preferred to be 0.08 dL/g or less.

For suppressing the hot spot of a solar cell module, it is preferred tomake the light reflection characteristic of the backside protectivemembrane uniform within a face. To cope with the trend of making thesize larger in recent years, uniformity of the light reflectivity in theprotective membrane face of at least 1 m×1.8 m which is the widely usedsize is demanded and, more preferably, uniformity of the lightreflectivity in a film roll is demanded. In the present invention, thein-face variation (maximum value−minimum value) of the light reflectanceof a film sample group collected by the sampling method which will bementioned later is preferred to be within 5%, more preferred to bewithin 4.5%, and further preferred to be within 4% to the mean value ofthe light reflectance. As a result thereof, generation of hot spot ofthe solar cell module can be advantageously suppressed.

When the film of the present invention is made into a roll, its woundlength is preferred to be 1500 m or longer and more preferred to be 1800m or longer. The upper limit of the wound length is preferred to be 5000m. Width of the film roll is preferred to be 500 mm or more and morepreferred to be 800 mm or more. Upper limit of the width of the filmroll is preferred to be 2000 mm.

The polyester film of the present invention can achieve high electricinsulation even if the film is thin. Further, due to its excellentdurability and reflectivity, the conventional durable layer(hydrolysis-resisting layer), white-colored layer and insulation layercan be integrated. Therefore, when the polyester film of the presentinvention is used as a sheet for sealing the backside of solar cell, itis now possible to cope with a demand for making the solar cell moduleinto light weight and thin membrane.

In the polyester film of the present invention, its partial dischargevoltage is preferred to be 550 V or higher, more preferred to be 560 Vor higher and further preferred to be 570 V or higher. When the partialdischarge voltage is within the above range, high electric insulation isachieved whereby that is advantageous for making the sealing sheet ofbackside of solar cell into thin membrane and also for making the solarcell module into large size.

Thickness of the polyester film of the present invention is preferably30 to 300 μm, more preferably 35 to 250 μm, further preferably 40 to 230μm, and furthermore preferably 40 to 200 μm. When the film thickness isless than the above lower limit, it is difficult to advantageouslyachieve the insulating effect while, when the thickness is more than theabove upper limit, it is no longer advantageous for making into lightweight and thin membrane as a sealing sheet for the backside of solarcell.

For controlling the partial discharge voltage to the above range, it ispreferred to form many cavities in the film. Generally, the cavitiesexisting in an insulation layer are the causes for the partialdischarge. It has been believed however that, when many fine cavitiesare generated in a film, voltage applied to the film is divided intofine cavities and the partial discharge voltage increases as a whole.Therefore, in making the partial discharge voltage high whilemaintaining the thinness of the film, it is preferred in the presentinvention that fine cavities are made to exist abundantly in thethickness direction.

In order to advantageously control the partial discharge voltage to theabove range, it is preferred that layered numbers of cavities existingin the thickness direction of the polyester film of the presentinvention are 5 or more and further that the density of layered numbersof cavities defined by the following formula satisfies the range of 0.1to 7/μm:

Density of layered numbers of cavities (numbers/μm)=[Layered numbers ofcavities in the thickness direction of film (numbers)]/[Thickness offilm (μm)]

The layered numbers of cavities existing in the thickness direction ofthe film is more preferred to be 7 or more and further preferred to be10 or more. As a result of increasing the numbers of fine cavitiesexisting in the thickness direction of the film, the partial dischargevoltage becomes advantageously high due to the voltage dispersingeffect.

With regard to the density of layered numbers of cavities existing inthe inner area of the cavity-containing film in view of the partialdischarge voltage, it is better when the density is more. However, whenit is too big, strength of the film is apt to lower. In order to makethe dielectric breakdown voltage high while maintaining the practicallynecessary film strength, it is preferred that the upper limit of theabove-mentioned density of layered numbers of cavities is made 5/μm and,more preferably, it is made one/μm.

Examples of a method for expressing the fine cavities in the filminclude (1) a method where a resin composition having a sea-islandstructure and comprising the polyester and a dispersion of thermoplasticresin which is not compatible with said polyester is extruded into asheet form and then stretched so as to form cavities (air) around theabove dispersion and (2) a method where a resin composition in whichparticles are made to contain in the polyester is extruded into a sheetform and then stretched so as to form cavities (air) around the aboveparticles. Between the above, the former method is preferred.

There is no particular limitation for the thermoplastic resin which isan island component being incompatible with the polyester. Although sucha resin may be either a homopolymer or a polymer having a copolymerizingcomponent, a material where polyolefin or polystyrene is a maincomponent is preferred. Further, the polystyrene is not always limitedto a homopolymer but may be a copolymerized polymer where variouscomponents are copolymerized.

A compounding amount of the thermoplastic resin being incompatible withthe polymer is preferred to be 1 to 30% by mass and more preferred to be5 to 18% by mass to the total materials used for the manufacture of thefilm. When it is less than 1% by mass, there is a limitation forincreasing the production amount of the cavities. On the contrary, whenit is more than 30% by mass, stretching property of the film issignificantly deteriorated and, moreover, there is a possibility thatheat resistance, strength and toughness are deteriorated.

Examples of the polyolefin include polyethylene, polypropylene,polymethylpentene, various kinds of cyclic olefin polymers andcopolymerized products thereof. Among the polyolefins as such,polymethylpentene is preferred since it rarely softens even at hightemperature and has an excellent cavity-expressing property. Whenpolymethylpentene is used as a main component of polyolefin, its soleuse is not always necessary but other polyolefin may be added also as anauxiliary component. Examples of the resin used as an auxiliarycomponent include polyethylene, polypropylene and products thereof beingcopolymerized with various components. It is preferred that the amountof the polyolefin added as an auxiliary component does not exceed theadding amount of the resin added as a main component.

As the polystyrene, there is a thermoplastic resin containing apolystyrene structure as a basic constituting element. Examples thereofinclude a homopolymer such as atactic polystyrene, syndiotacticpolystyrene or isotactic polystyrene; a modified resin where othercomponent is subjected to graft or block copolymerization such asshock-resisting polystyrene resin and modified polyphenylene etherresin; and a mixture with a thermoplastic resin being compatible withthose polystyrene resins such as polyphenylene ether.

The polyester film of the present invention may be in a single layer orin a laminated structure comprising two or more layers. The film of thepresent invention is often used as a component for a solar cell by beinglaminated with other constituting layer and, when cavities in the filmare present near the surface, strength of the film surface lowers andinterface detachment is apt to happen. Accordingly, the film of thepresent invention may also be made into such a laminated structure whichconsists of a skin layer comprising a polyester layer where manyinorganic fine particles exist and of a core layer comprising apolyester layer containing many cavities derived from thermoplasticresin being incompatible with the polyester.

When the film is made into a three-layered constitution consisting of acore layer and two skin layers sandwiching the former, it is preferredthat the thickness ratio of the skin layer to the core layer is 5 to20%, more preferred to be 8 to 18% and further preferred to be 10 to 15%in terms of the skin layer thickness (total thickness of both skinlayers) to the total layer thickness of the film. When the ratio of theskin layer thickness is less than the above lower limit, surficialstrength of the film lowers and, when it is layered with other layer asa sealing sheet for a solar cell, detachment between the layers is aptto happen. When the ratio of the skin layer thickness is more than theabove upper limit, layered numbers of cavities by a core layer becomesdifficult to secure and an electric insulation property is hardly apt tobe achieved.

In the film of the present invention, its apparent specific gravity ispreferred to be 0.8 to 1.3, more preferred to be 0.9 to 1.3, and furtherpreferred to be 1.0 to 1.2. When the apparent specific gravity is lessthan 0.8, the film is not tough and a process for the preparation of asolar cell module is difficult. Particularly when the size of a sealingsheet for the backside becomes large, a buckling property in broad widthis apt to happen. When the apparent specific gravity is more than 1.3,weight of the film is big whereby there is a possibility that it becomesa burden in the case of reducing the weight of the solar cell.

Although there is no particular limitation for the method ofmanufacturing a film in a layered constitution, it is preferred toadopt, for example, a co-extrusion method where a polyester resin of theskin layer containing fine particles and a polyester resin of the corelayer containing an incompatible thermoplastic resin are supplied todifferent extruders, layered in a melted state and extruded from thesame die.

The polyester chip is melted in an extruder by the above method and theresin is pulled out in a sheet form from a die using a cooling rollwhereupon a non-stretched film is formed. In that case, it is preferredto use a well-dried polyester chip so as to suppress an increase in theacid value during the manufacture of a film. Moisture content of thepolyester chip used therefor is preferred to be 100 ppm or less, morepreferred to be 50 ppm or less, and further preferred to be 30 ppm orless. As a method for drying a polyester chip, a known method such asvacuum drying may be used.

The highest temperature of the polyester resin in an extruder ispreferred to be 280° C. to 310° C. and more preferred to be 290° C. to300° C. When the melting temperature is made high, back pressure uponfiltration in an extruder lowers and good productivity can be achievedbut, when the resin temperature is made higher than 310° C., there maybe the case where thermal deterioration of the resin proceeds and acidvalue of the polyester increases whereupon the resistance to hydrolysislowers.

Then, after the resulting non-stretched film is heated with a heatingroll or a non-contacting heater, it is stretched between rolls havingthe difference between their speeds (roll stretch), then both ends ofthe uniaxially stretched film are held by clips, heating is conducted inan oven, stretch is carried out in a widthwise direction andhigh-temperature heat is applied to conduct a thermal setting (tenterstretch). It is also possible to conduct a biaxial alignment treatmentby means of, for example, a simultaneous biaxial stretch (simultaneousbiaxial stretch by tenter) where stretch is done using a tenter having amechanism for conducting a simultaneous stretch in both longitudinal andtransverse directions or a stretch by expansion using air pressure(inflation stretch).

As a result of such an orientation treatment, interface detachmentbetween the polyester and the incompatible thermoplastic resin orbetween the polyester and the fine particles is resulted whereupon manyfine cavities are expressed. Accordingly, the conditions for subjectingthe non-stretched sheet to a stretching and orientation treatment areclosely related to the formation of cavities.

When a more highly dimensional stability against heating is demanded asa solar cell component, it is desirable to apply a longitudinalrelaxation treatment. As a method for the longitudinal relaxationtreatment, there may be utilized, for example, a method where alongitudinal relaxation is conducted by making the space between theclips of the tenter gradually narrow or a method where relaxationtreatment is conducted by avoiding the influence of the clips by meansof cutting the edge using a razor in a tenter. It is also possible touse a method where an off-line heat is applied to relax. The thermalshrinking rate in longitudinal and transverse directions is preferred tobe within a range of 0 to 4.0% and more preferred to be within a rangeof 0.2 to 3.0%. When the thermal shrinking rate is in a negative value,the film slackens upon processing and that causes a problem. When thethermal shrinking rate is more than 4.0%, the shrinkage upon processingis big whereby washboard-like wrinkles are generated and that is notpreferred.

Further, for imparting various functions such as adhesive property,insulating property and anti-scratching property, a polymer resin may becoated on the film surface by a coating method. Still further, inorganicand/or organic particles may be made to contain only in the coatinglayer so as to make into an easily slidable polyester film. Stillfurther, inorganic vapor deposition layer or aluminum layer may beformed to impart a barrier function to steam vapor. In the film of thepresent invention however, it is preferred that the film surface is flatand smooth when it is used as a sealing sheet for the backside bylayering with other layer. In that case, the three-dimensional surfaceroughness (SRa) of the film of the present invention is preferred to be0.1 μm or less.

When an applied layer having an easy adhesive property is formed on thepolyester film of the present invention, it is preferred to use anaqueous applying solution containing at least one of water-soluble orwater-dispersible copolymerized polyester resin, acrylic resin andpolyurethane resin. Examples of the applying solution includewater-soluble or water-dispersible copolymerized polyester resinsolution, acrylic resin solution and polyurethane solution which aredisclosed, for example, in Japanese Patent No. 3,567,927, JapanesePatent No. 3,589,232 and Japanese Patent No. 3,589,233. Such an appliedlayer may be formed after making into a film (off-line coating method)or may be formed during making into a film (in-line coating method). Inview of the productivity, it is preferred to form during the course ofmaking into a film.

Particularly when the film of the present invention is used in a facecontacting an encapsulation foil such as EVA, it is preferred that thefilm of the present invention has an adhesive property to EVA. In thatcase, a urethane resin can be used as a main component. Particularlywhen the urethane resin where aliphatic polycarbonate polyol is aconstituting component is made to contain in the applied layer, anadhesive property as a solar cell component under moisture- andheat-resistance can be enhanced. It is preferred that an aliphaticpolycarbonate polyol having an excellent resistance to heat andhydrolysis is made to contain in a diol component which is aconstituting component of the urethane resin. In view of prevention ofyellowing by sunlight as well, it is preferred to use an aliphaticpolycarbonate polyol.

Examples of the aliphatic polycarbonate polyol include aliphaticpolycarbonate diol and aliphatic polycarbonate triol. Number-averagemolecular weight of the aliphatic polycarbonate polyol is preferred tobe 1500 to 4000 and more preferred to be 2000 to 3000. When thenumber-average molecular weight of the aliphatic polycarbonate polyol istoo small, a strong and hard urethane component increases and stress dueto thermal shrinkage of the substrate cannot be relaxed any more wherebythere may be the case where the adhesive property lowers.

When a polyol compound having a carboxylic acid (carboxylate) group isused as a copolymerizing component for imparting a water solubility, thecomposing molar ratio of the polyol compound having carboxylic acid(carboxylate) group in the urethane resin is preferred to be 3 to 60molar % and more preferred to be 5 to 40 molar % in case the totalpolyisocyanate component in the urethane resin is 100 molar %. When theabove composing molar ratio is less than 3 molar %, there may be thecase where dispersibility in water lowers. When the above compositionmolar ratio is more than 60 molar %, there may be the case whereresistance to water lowers whereby resistance to moist heat lowers.

Glass transition temperature of the urethane resin is preferred to belower than 0° C. and more preferred to be lower than −5° C. When theglass transition temperature is lower than 0° C., viscosity of theurethane resin becomes near the viscosity of the partially melted olefinresin such as EVA or PVB upon adhesion with pressure whereby itcontributes in enhancing the strong adhesion due to partial mixing andsoftness which is advantageous in view of relaxation of stress of theapplied layer is apt to be achieved.

In the polyester film of the present invention, the retaining rate ofelongation at 105° C., 100% RH and 0.03 MPa for 192 hours is preferredto be 65% or more and more preferred to be 70% or more. When theretaining rate of elongation is within such a range, the polyester filmof the present invention can achieve high resistance to hydrolysis beingdurable for a long-term outside use.

In the polyester film of the present invention, its thermal shrinkingrate at 150° C. is preferred to be −0.5% to 3.0% and more preferred tobe −0.5% to 2.0% in both lengthwise direction (longitudinal direction)and widthwise direction (transverse direction). When there is a demandfor severer thermal shrinking rate as a solar cell such as precision inthe use at high temperature or in the process at high temperature, itsthermal shrinking rate at 150° C. is preferred to be −0.5% to 0.5% inboth lengthwise direction (longitudinal direction) and widthwisedirection (transverse direction). As a result thereof, it is possible tosuppress the generation of curl upon a heating process (such as uponformation of an adhesive layer) or in a layered state. An example of amethod for making the thermal shrinking rate at 150° C. within the aboverange is a method where the stretching condition is controlled or wherelongitudinal relaxation treatment and transverse relaxation treatmentare conducted during a thermal setting step.

For retaining the breaking elongation of the film, it is preferred thatorientations of the film in longitudinal and transverse directions arewell balanced. MOR value converted to the case where the film thicknessof the polyester film of the present invention is 50 μm (MOR-C) ispreferred to be 1.0 to 2.0 and more preferred to be 1.3 to 1.8. As aresult thereof, balance of the film in longitudinal and transversedirections can be adjusted and that is effective in maintaining themechanical strength and durability. Generation of curl upon layering canbe also suppressed thereby and that is effective for enhancing the closeadhesion as well. An example of a method for making the MOR-C within theabove range is a method where the ratio of stretching magnifications inlongitudinal and transverse directions during the stretching step iscontrolled.

The solar cell module of the present invention is a system whereincident light such as sunlight or room light is received and convertedinto electricity and the resulting electricity is stored. Said module isconstituted from surface protecting sheet, high transmission materialfor light, solar cell device, encapsulation foil layer, backside sealingsheet, etc.

The polyester film of the present invention can be used as abase filmfor a backside sealing sheet or a laminating material for flexibleelectronic components. It is particularly advantageous as abase film fora backside sealing sheet for a solar cell where high durability andlong-term thermostability are demanded. The backside sealing sheet isapplied for protecting the backside of a solar cell device of a solarcell module.

The polyester film of the present invention can be used for the face ofthe side contacting the encapsulation foil of the solar cell moduleand/or for the outermost face of the solar cell module as a backsidesealing sheet either solely or by adhering two or more sheets. For apurpose of imparting a barrier property against water vapor, thebackside sealing sheet may be layered with a film or an aluminum foilhaving a barrier property against water vapor. As the film having abarrier property, there may be used poly(vinylidene fluoride)-coatedfilm, silicon oxide-deposited film, aluminum oxide-deposited film,aluminum-deposited film, etc. They may be used by layering to thepolyester film of the present invention either directly or via anadhesive layer or in a form of a sandwiched structure.

EXAMPLES

Examples and Comparative Examples of the present invention will be shownas hereunder. Methods for measurement and evaluation used in the presentinvention are as follows:

1) Apparent Density of the Film

Apparent density of the film was measured according to JIS-K-7222“Foamed plastics and rubbers—measurement of apparent density”. Forsimplifying the expression, its unit was calculated in g/cm³.

2) Degree of Whiteness

Degree of whiteness was measured according to JIS-L1015-1981-method Busing Z-1001DP manufactured by Nippon Denshoku Kogyo.

3) Acid Value

Acid value was measured by the following method for the film and thematerial polyester resin:

(1) Preparation of Samples

Film or material polyester resin was ground, dried in vacuo at 70° C.for 24 hours and weighed within a range of 0.20±0.0005 g using abalance. The mass at that time was W (grams). Benzyl alcohol (10 ml) andthe weighed sample were added to a test tube, the test tube was dippedin a benzyl alcohol bath heated at 205° C. and the sample was dissolvedby stirring with a glass rod. The samples when the dissolving time was3, 5 and 7 minutes were called A, B and C, respectively. After that, afresh test tube was provided, only benzyl alcohol was placed therein,the same treatment as above was conducted and the samples where thedissolving time was 3, 5 and 5 minutes were called a, b and c,respectively.

(2) Titration

Titration was conducted using 0.04 mol/l potassium hydroxide solution(ethanolic solution) for which a factor was already known. Phenol Redwas used as an indicator and a titrated amount (ml) of potassiumhydroxide solution was determined at the end point which was a stagewhen yellowish green color turned pale red color. Titrated amounts forthe samples A, B and C were called XA, XB and XC (ml), respectively.Titrated amounts for the samples a, b and c were called Xa, Xb and Xc(ml), respectively.

(3) Calculation of Acid Value

The titrated amounts XA, XB and XC for each dissolving time were usedand the titrated amount V (ml) when the dissolving time was 0 minute wascalculated by means of a least-squares method. Similarly, using Xa, Xband Xc, the titrated amount V0 (ml) was determined. After that, an acidvalue was calculated by the following formula.

Acid value (eq/ton)=[(V−V0)×0.04×NF×1000]/W

NF: Factor for 0.04 mol/l potassium hydroxide solution

4) Treatment for Resistance to Hydrolysis

As a treatment for resistance to hydrolysis, HAST (Highly Acceleratedtemperature and humidity Stress Test) stipulated by JIS-60068-2-66 wasconducted. As an instrument, EHS-221 manufactured by Espec was used andthe test was conducted under the conditions of 105° C., 100% RH and 0.03MPa.

The film was cut into 70 mm×190 mm and the films were placed using ajig. Each film was placed keeping intervals among the films so that thefilm does not touch each other. The treatment was conducted for 200hours under the conditions of 105° C., 100% RH and 0.03% MPa.

5) Treatment for Resistance to Light

As a treatment for accelerated resistance to light, a continuous UVirradiation treatment was conducted for 100 hours at 63° C., 50% RH and100 mW/cm² irradiation intensity using Eye Super UV Tester SUV-W151manufactured by Iwasaki Electric.

6) Retaining Rate of Breaking Elongation

Resistance to hydrolysis and resistance to light were evaluated by aretaining rate of breaking elongation. The breaking elongations beforeand after each of the treatments were measured according toJIS-C-2318-1997 5.3.31 (Tensile strength and elongation percentage) andthe retaining rate of breaking elongation was calculated by thefollowing formula:

Retaining rate of breaking elongation (%)=[(Breaking elongation afterthe treatment)×100]/(Breaking elongation before the treatment)

7) Layered Numbers of the Cavities Existing in the Thickness Directionof the Film and the Density of Layered Numbers of the Cavities of theFilm

A scanning electron microscope was used for observation of the cavitieson the section of the film and, in five places of different sites of asample, a broken section which was parallel to the longitudinal stretchdirection and vertical to the film surface was observed. The observationwas conducted in the appropriate magnifications of 300 to 3000 andpictures were taken in such a manner that the dispersed state of thecavities in the total thickness of the film can be confirmed. Afterthat, at any place on the photographic picture, a straight line wasdrawn in a vertical direction to the film surface and the cavity numberscrossing this straight line were counted. This cavity numbers aredefined as the cavity numbers (layered numbers) in the thicknessdirection of the film. Further, total thickness (μm) of the film wasmeasured along this straight line and the layered numbers of cavitiesare divided by the total thickness of the film to determine the densityof layered numbers of cavities (numbers/μm). The measurement was done atfive places for one sheet of the picture and a mean value of 25 placesin total were defined as the density of layered numbers of cavities of asample.

8) Thermal Shrinkage Rate of the Film at 150° C. (HS150)

Film was cut into a size of 10 mm width and 250 mm length in such adirection that the long side (250 mm) corresponds to a lengthwise orwidthwise direction of the film, and marked at 200-mm intervals and theinterval (A) was measured with a constant tension of 5 g. After that,the film was allowed to stand for 30 minutes in an oven of atmosphere of150° C. without load. After the film was taken out from the oven andcooled down to room temperature, the mark interval (B) was determinedwith a constant tension of 5 g and thermal shrinkage rate was calculatedby the following formula:

Thermal shrinkage rate (%)=[(A−B)/A]×100

The thermal shrinkage rate of the film at 150° C. was measured at 100-mmintervals in the widthwise direction of the film, mean value of threesamples was rounded off to two decimal places and the larger values inlengthwise direction and widthwise direction were used.

9) Measurement of Partial Discharge Voltage

Partial discharge voltage was measured according to the followingmeasuring method to evaluate the electric insulation property:

(Measuring Method)

Standards used: IEC60664/A2:2002 4.1.2.4

Testing machine: KPD2050 (manufactured by KIKUSUI ELECTRONICS CORP.)

Starting voltage charge threshold value: 1.0 pC

Extinction voltage charge threshold value: 1.0 pC

Testing time: 22.0 s

Measured pattern: trapezoid

10) Limiting Viscosity (IV)

After the film or the polyester resin was ground and dried, it wasdissolved into a mixed solvent of phenol/tetrachloroethane (=60/40;ratio by weight). After this solution was subjected to a centrifugaltreatment to remove inorganic particles, running-down time of a solutionof 0.4 (g/dl) and that of the solvent only were measured at 30° C. usinga Ubbelohde's viscometer. From their time ratio, a limiting viscositywas calculated using a Huggins formula with a presumption that Hugginsconstant was 0.38.

11) Light Reflectance

In the resulting film roll, start and end of roll winding were defined0% and 100%, respectively and a film piece of 1 m×1.8 m was cut out fromthe central area at each of the length positions 10%, 50% and 90%. Fivefilm samples in regular squares of 20 cm square were sampled from fourcorners and the center of each film piece. The reflectance of a standardwhite board (manufactured by Hitachi High Technologies; Parts No.210-0740) was measured by a spectrophotometer (U-3500; manufactured byHitachi). With regard to each of the 15 film samples in total, the valueat 550 nm wavelength was adopted as a light reflectance from therelative reflectance to the reflectance of a standard white board takenas 100%. Mean value of the light reflectances in each film sample wasused as a central value and the value obtained after dividing thedifference between the maximum and the minimum values of the resultinglight reflectance by the central value was adopted as the variation ofthe light reflectance. Incidentally, the light reflectance in the tableshows the resulting central value.

12) MOR-C

The resulting film was divided into five equal parts in a widthwisedirection, a sample in regular square (100 mm in longitudinal andwidthwise directions) was prepared in each position and measurement wasconducted using a microwave permeation molecular orientation meter(MOA-6004 manufactured by Oji Keisoku Kiki). MOR-C was measured with thethickness correction of 50 μm and a mean value of five points was used.

13) Content of Diethylene Glycol (DEG)

Content of diethylene glycol was determined by means of gaschromatographic quantification after degradation of 0.1 g of thepolyester by heating at 250° C. in 2 ml of methanol.

14) Surface Strength

The film was cut out into a size of 5 cm and 20 cm in longitudinal andtransverse directions, respectively and its whole surface was adheredonto a flat glass plate using a polyester double-sided adhesive tape. Anadhesive tape (manufactured by Nichiban; Cellotape (registered trademark)) of 24 mm width was adhered onto the surface thereof over a lengthof 35 mm followed by being allowed to stand for 1 minute. After that,the tape was peeled off at a time in a direction of being vertical tothe glass surface and the surface was observed. When the film surfacewas peeled off to an extent of 50% or more of the peeled area of theadhesive tape B, it was defined as “peeled off”. In case the frequencyof “peeled off” was less than one half upon five or more repetitions, itwas evaluated as “∘” (surface strength was excellent) while, incase theabove was one half or more, it was evaluated as “x” (surface strengthwas inferior).

15) Strength Upon Processing

The film cut out into a size of 1 m×1.5 m was adhered in flat sheets andinstalled in an apparatus (LM-50×50S manufactured by NPC). Afterprocessing 50 sheets, outer appearances of all sheets were observed.When no bending was noted for all films, it was evaluated as “∘” while,when one or more film(s) was/were bent, it was evaluated as “x”.

16) Surface Flatness

Both surfaces of the film were measured using a three-dimensionalroughness tester of stylus type (SE-3AK; manufactured by KosakaKenkyusho), under the conditions where needle radius was 2 load was 30mg, cut-off value was 0.25 mm, measuring length was 1 mm, and movingspeed of a needle was 0.1 mm/second, then the result was divided into500 points with 2-μm pitch and the height of each point was put into athree-dimensional roughness analyzer (SPA-11). After that, averagecentral surface roughness (SRa) was determined using the analyzer. WhenSRa of both sides of the film was 0.1 μm, it was evaluated as “∘”.

(Preparation of Polyester Resin Pellets)

Manufacture of PET Resin (PET-I)

Temperature of an esterifying reactor was raised and, when it reached200° C., a slurry comprising 86.4 parts by mass of terephthalic acid and64.4 parts by mass of ethylene glycol was charged and, as a catalysts,0.017 part by mass of antimony trioxide and 0.16 part by mass oftriethylamine were added thereto with stirring. Then the temperature wasraised with pressure and, under the condition where gauge pressure was3.5 kgf/cm² and temperature was 240° C., an esterification reaction wasconducted under pressure. After that, inside of the esterificationreactor was returned to atmospheric pressure, 0.071 part by mass ofmagnesium acetate tetrahydrate was added and then 0.014 part by mass oftrimethyl phosphate was added thereto. Then the temperature was furtherraised up to 260° C. within 15 minutes, 0.012 part by mass of trimethylphosphate was added and then 0.0036 part by mass of sodium acetate wasadded thereto. After 15 minutes, the resulting esterifying reactionproduct was transferred to a polycondensation reactor, the temperaturewas gradually raised from 260° C. to 280° C. in vacuo and apolycondensation reaction was carried out at 285° C.

After completion of the polycondensation reaction, a filtrationtreatment was conducted using a filter made of NASLON where a 95%-cutradius was 5 μM, the filtrate was extruded from a nozzle into a strandshape and cooled/solidified using a cooling water which was previouslysubjected to a filtering treatment (pore size: 1 μm or less) and theresulting one was cut into pellets. Limiting viscosity and acid value ofthe resulting PET resin (PET-I) were 0.616 dL/g and 15.1 eq/ton,respectively. Neither inactive particles nor particles separated intoinside were substantially contained therein.

Manufacture of PET Resin (PET-II)

After the PET resin (PET-I) was previously subjected to preliminarycrystallization at 160° C., it was subjected to a solid-phasepolymerization under a nitrogen atmosphere at the temperature of 220° C.to give a PET resin (PET-II) having limiting viscosity of 0.71 L/g anacid value of 11 eq/ton.

Manufacture of PET Resin (PET-III)

The PET resin (PET-I) was subjected to the same method for themanufacture of PET-II except that the time for polycondensation reactionwas changed to give a PET resin (PET-III) having limiting viscosity of0.510 dL/g and acid value of 39 eq/ton.

Manufacture of PET Resin (PET-IV)

(Preparation of Polycondensation Catalyst Solution)

(Preparation of Ethylene Glycol Solution of Phosphorus Compound)

After 2.0 liters of ethylene glycol was added to a flask equipped with anitrogen introducing pipe and a cooling jacket at ambient temperatureand under atmospheric pressure, 200 g of Irganox 1222 (manufactured byCiba Specialty Chemicals) was added as a phosphorus compound withstirring at 200 rpm in a nitrogen atmosphere. More 2.0 liters ofethylene glycol was additionally added thereto, temperature was raisedby changing the temperature set for the jacket to 196° C. and, as fromthe stage when the inner temperature reached not lower than 185° C.,stirring was conducted under refluxing for 60 minutes. After that, theheating was discontinued and the solution was immediately removed fromthe heat source and cooled down to 120° C. or lower within 30 minuteswhile the nitrogen atmosphere was still maintained. Mole fraction ofIrganox 1222 in the resulting solution was 40% and that of a compoundwherein the structure was changed from Irganox 1222 in the resultingsolution was 60%.

(Preparation of Aqueous Solution of Aluminum Compound)

After 5.0 liters of pure water was added to a flask equipped with acooling jacket at ambient temperature and under atmospheric pressure,200 g of basic aluminum acetate was added as a slurry in pure water withstirring at 200 rpm. Pure water was further added so as to make 10.0liters as a whole followed by stirring for 12 hours at ambienttemperature and under atmospheric pressure. After that, temperature wasraised by changing the temperature set for the jacket to 100.5° C. and,as from the stage when the inner temperature reached not lower than 95°C., stirring was conducted under refluxing for 3 hours. The stirring wasdiscontinued and temperature was lowered down to room temperature togive an aqueous solution.

(Preparation of Ethylene Glycol Solution of Aluminum Compound)

The equivalent volume of ethylene glycol was added to an aqueoussolution of aluminum compound prepared hereinabove, the mixture wasstirred at room temperature for 30 minutes, the inner temperature wascontrolled to 80 to 90° C., the pressure was gradually reduced to reach27 hPa and water was evaporated from the system by stirring for severalhours to give an ethylene glycol solution of aluminum compound of 20g/l. Peak integral value ratio in ²⁷Al-NMR spectrum of the resultingaluminum solution was 2.2.

(Esterifying Reaction and Polycondensation)

There was provided a continuous polyester manufacturing apparatuscomprising three continuous esterifying reactors and threepolycondensation reactors and having an in-line mixer with a high-speedstirrer being installed in a transfer line from the third esterifyingreactor to the first polycondensation reactor. Ethylene glycol (0.75part by mass) to 1 part by mass of highly pure terephthalic acid wascontinuously supplied to a slurry-preparing tank in the above apparatus.The prepared slurry was continuously supplied and, under such reactionconditions where reaction temperatures and pressures of the first,second and third esterifying reactors were 250° C. and 110 kPa; 260° C.and 105 kPa; and 260° C. and 105 kPa, respectively, 0.025 part by massof ethylene glycol was continuously poured into the second esterifyingreactor to give a polyester oligomer. The oligomer was continuouslytransferred to a continuous polycondensation apparatus comprising threereactors. At the same time, the ethylene glycol solution of a phosphoruscompound and the ethylene glycol solution of an aluminum compoundprepared hereinabove were continuously added to an in-line mixerinstalled in the transfer line together with stirring using a mixer of astirring type so that content of aluminum atom and content of phosphorusatom were made 0.015 molar % and 0.036 molar %, respectively, to acidcomponent in the polyester. Then, polycondensation was carried out undersuch reaction conditions that reaction temperatures and pressures of theinitial, intermediate and final polycondensation reactors were 265° C.and 9 kPa; 265 to 268° C. and 0.7 kPa; and 273° C. and 13.3 kPa,respectively to give a PET resin (PET-IV) having limiting viscosity of0.630 dL/g and acid value of 10.5 eq/ton.

Manufacture of PET Resin (PET-V)

Solid-phase polymerization was conducted from PET resin (PET-IV) using arotary vacuum polymerization reactor under reduced pressure of 0.5 mmHgat 220° C. for different reaction time to prepare a PET resin (PET-V)having limiting viscosity of 0.73 dL/g and acid value of 5.0 eq/ton.

Manufacture of PET Resin (PET-VI)

Solid-phase polymerization was conducted from PET resin (PET-IV) using arotary vacuum polymerization reactor under reduced pressure of 0.5 mmHgat 220° C. for different reaction time to prepare a PET resin (PET-VI)having limiting viscosity of 0.79 dL/g and acid value of 4.0 eq/ton.

Manufacture of PET Resin (PET-VII)

Solid-phase polymerization was conducted from PET resin (PET-IV) using arotary vacuum polymerization reactor under reduced pressure of 0.5 mmHgat 220° C. for different reaction time to prepare a PET resin (PET-VII)having limiting viscosity of 0.69 dL/g and acid value of 7.0 eq/ton.

Manufacture of PET Resin (PET-VIII)

Solid-phase polymerization was conducted from PET resin (PET-IV) using arotary vacuum polymerization reactor under reduced pressure of 0.5 mmHgat 220° C. for different reaction time to prepare a PET resin (PET-VIII)having limiting viscosity of 1.01 dL/g and acid value of 3.0 eq/ton.

Manufacture of Master Batch Containing Fine Particles

Manufacture of Master Batch (MB-I) Containing Fine Particles

As a material, a mixture of 50% by mass of a PET resin (PET-I)previously dried at 120° C. in 10⁻³ torr for about 8 hours with 50% bymass of rutile-type titanium dioxide having an average particle size of0.3 μm (according to an electron microscopic method) was supplied to abiaxial vent-type extruder and extruded at 275° C. together withdeaeration by kneading to prepare master bath (MB-I) pellets containingfine particles of rutile-type titanium dioxide. Limiting viscosity andacid value of the resulting pellets were 0.45 dL/g and 42.2 eq/ton,respectively.

Manufacture of Master Batch (MB-II) Containing Fine Particles

Solid-phase polymerization was conducted from the above master batch(MB-I) pellets containing fine particles of rutile type titanium oxideusing a rotary vacuum polymerization reactor under reduced pressure of0.5 mmHg at 220° C. for different reaction time to prepare a masterbatch (MB-II) containing fine particles of rutile type titanium oxideand having limiting viscosity of 0.71 dL/g and acid value of 23.5eq/ton.

Manufacture of Master Batch (MB-III) Containing Fine Particles

The same method as in the case of the master batch (MB-I) containingfine particles was conducted except that PET resin (PET-IV) was usedinstead of PET resin (PET-I) whereupon a master batch (MB-III)containing fine particles of rutile type titanium dioxide was prepared.Limiting viscosity and acid value of the resulting pellets were 0.46dL/g and 36.3 eq/ton, respectively.

Manufacture of Master Batch (MB-IV) Containing Fine Particles

Solid-phase polymerization was conducted from the above master batch(MB-III) pellets containing fine particles of rutile type titanium oxideusing a rotary vacuum polymerization reactor under reduced pressure of0.5 mmHg at 220° C. for different reaction time to prepare a masterbatch (MB-IV) containing fine particles of rutile type titanium oxideand having limiting viscosity of 0.70 dL/g and acid value of 19.4eq/ton.

Manufacture of Cavity-Forming Agent (MB-V)

As a material, 20% by mass of polystyrene (manufactured by JapanPolyStyrene Inc.; G797N) having melt flow rate of 1.5, 20% by mass ofpolypropylene (manufactured by Idemitsu Kosan Co., Ltd.; F300SP)prepared by a gas-phase polymerization and having melt flow rate of 3.0,and 60% by mass of polymethylpentene (manufactured by Mitsui Chemicals,Inc.; TPX DX-820) having melt flow rate of 180 were subjected to apellet mixing, supplied to a biaxial extruder and well kneaded to give acavity-forming agent (MB-V).

Manufacture of Master Batch (MB-VI) Containing Fine Particles

Solid-phase polymerization was conducted from the above master batch(MB-III) pellets containing fine particles of rutile type titanium oxideusing a rotary vacuum polymerization reactor under reduced pressure of0.5 mmHg at 220° C. for different reaction time to prepare a masterbatch (MB-VI) containing fine particles of rutile type titanium oxideand having limiting viscosity of 0.80 dL/g and acid value of 17.2eq/ton.

Example A1 Preparation of Film

A mixture of 65% by mass of polyethylene terephthalate resin (PET-II)and 35% by mass of the previously-prepared MB-II was used as a materialfor a layer A while a mixture of 85% by mass of PET-II, 7% by mass ofMB-II and 8% by mass of MB-V was used as a material for a layer B. Eachof them was poured into separate extruder, mixed and melted at 285° C.and conjugated in a melted state so as to give A/B/A layers by using afeed-block. At that time, the rate of extruding amounts for the layer Ato the layer B was controlled using a gear pump. After that, the abovewas extruded using a T-die onto a cooling drum adjusted to 30° C.whereupon a non-stretched sheet was prepared.

(Preparation of Biaxially Stretched Film)

The resulting non-stretched sheet was uniformly heated at 75° C. using aheating roll and subjected to a roll stretch of 3.3 times by heating at100° C. using a non-contacting heater. The resulting uniaxiallystretched film was introduced to a tenter, subjected to a transversestretch of 4.0 times by heating at 140° C., subjected to a heatingtreatment at 215° C. for 5 seconds by fixing its width and furthersubjected to a 4% relaxation treatment at 210° C. in a widthwisedirection. Both ends were trimmed, the resulting one was wound using awinding apparatus and slit by dividing into equal two parts in awidthwise direction to give a polyester film for sealing the backside ofsolar cell having 1300 mm width, 3000 m length and 50 μm thickness(A/B/A=3/44/3 μm).

Example A2

The same method as in Example A1 was conducted except that the extrudedamount and the speed were adjusted whereupon a polyester film forsealing the backside of solar cell having 125 μm thickness (8/109/8 μm)was prepared.

Example A3

The same method as in Example A1 was conducted except that the extrudedamount and the speed were adjusted whereupon a polyester film forsealing the backside of solar cell having 188 μm thickness (11/166/11μm) was prepared.

Example A4

The same method as in Example A1 was conducted except that the resultingnon-stretched film was uniformly heated at 75° C. using a heating rollfollowed by heating at 100° C. using a non-contacting heater to conducta roll stretch of 3.5-times whereupon a polyester film for sealing thebackside of solar cell having 50 μm thickness was prepared.

Example A5

The same method as in Example A1 was conducted except that, in order toform a layer B, PET-II was mixed with 5% by mass of polymethylpentene(manufactured by Mitsui Chemicals, Inc.; TPX; DX820) and 10% by mass ofa copolymerized PET containing 10% by mass of polyethylene glycol having4,000 molecular weight as a dispersing agent whereupon a polyester filmfor sealing the backside of solar cell having 50 μm thickness wasprepared.

Example A6

The film roll prepared in Example A1 was passed through an off-linecoater set at the temperature of 160° C. and subjected to a relaxationtreatment by adjusting the speed and the tension whereupon a polyesterfilm for sealing the backside of solar cell having 50 μm thickness wasprepared.

Example A7

The same operation as in Example A1 was conducted except that a mixtureof 65% by mass of polyethylene terephthalate resin (PET-V) with 35% bymass of MB-IV was used as a material for the layer A and that a mixtureof 85% by mass of PET-V, 7% by mass of MB-IV and 8% by mass of MB-V wasused as a material for the layer B whereupon a polyester film forsealing the backside of solar cell having 50 μm thickness was prepared.

Example A8 Compounding of Applying Solution

(Polymerization of Urethane Resin Solution I where AliphaticPolycarbonate Polyol is Constituting Component)

4,4-Diphenylmethane diisocyanate (43.75 parts by mass), 12.85 parts bymass of dimethylolbutanoic acid, 153.41 parts by mass ofpolyhexamethylenecarbonate diol of 2000 number-average molecular weight,0.03 part by mass of dibutyl tin dilaurate and 84.00 parts by mass ofacetone (as a solvent) were poured into a container and stirred at 75°C. for 3 hours in a nitrogen atmosphere, temperature of the resultingreaction solution was lowered to 40° C. and 8.77 parts by mass oftriethylamine was added thereto whereupon a polyurethane prepolymersolution was prepared. Water (450 g) was added thereto, the mixture wasadjusted to 25° C. and, with stirring/mixing at 2000 min⁻¹, thepolyurethane prepolymer solution was added thereto so that it wasdispersed in water. After that, a part of water and acetone were removedin vacuo to prepare a water-soluble polyurethane resin solution Icontaining 35% of solid. Glass transition temperature of the resultingpolyurethane resin I was −30° C.

(Preparation of Applying Solution)

The following applying agents were mixed to prepare an applyingsolution.

Water 55.86% by mass Isopropanol 30.00% by mass Polyurethane resinsolution I 13.52% by mass Particles (silica sol of 40 nm averageparticle size;  0.59% by mass solid concentration: 40% by mass)Surfactant (silicone type; solid concentration: 100%  0.03% by mass bymass)

The above applying solution was applied by a roll coat method to oneside of the uniaxially orientated PET film after a longitudinal stretchin Example A1 and, after that, drying was conducted at 80° C. for 20seconds. Incidentally, an adjustment was conducted so as to make theapplied amount after the final drying (after a biaxial stretch) 0.15g/m². After that, stretch was conducted using a tenter by the samemethod as in Example A1 to give a polyester film for sealing thebackside of solar cell having 50 μm thickness.

The resulting film was cut out into a size of 100 mm width×100 mm lengthwhile the EVA sheet was cut out into a size of 70 mm width×90 mm lengthand they were layered in a constitution of [film (applying layerside)/EVA mentioned below/(applying layer side) film] followed bysubjecting to a pressure connection together with heating using a vacuumlaminator under the following adhering condition whereupon a sample wasprepared. The prepared sample still showed a good adhesive property evenafter being allowed to stand for 1000 hours in a container of hightemperature and high humidity under the atmosphere of 85° C. and 85% RH.

(Adhering Condition)

Apparatus: Vacuum laminator manufactured by NPC, Inc., LM-30×30 type

Pressure: 1 atmospheric pressure

EVA: manufactured by Sanvic, Ultrapearl PV (0.4 μm)

Laminating step: at 100° C. (for 5 minutes in vacuo and for 5 minuteswith pressure in vacuo)

Curing step: thermal treatment at 150° C. (at ordinary pressure for 45minutes)

Example A9 Manufacture of Back Sheet for Solar Cell

A layer constitution of [(polyester film for sealing the backside ofsolar cell of Example A1)/(polyester film, manufactured by Toyobo; A4300125 μm)/(polyester film for sealing the backside of solar cell ofExample A1)] was adhered by a dry lamination method to give a sheet forsealing the backside of solar cell. When partial discharge voltage ofthe resulting sheet for sealing the backside of solar cell was measured,it was 1090 V.

(Adhesive for Dry Laminate)

(Takelac A-315 manufactured by Mitsui Chemicals, Inc.)/(Takenate A-10manufactured by Mitsui Chemicals, Inc.)=9/1 (ratio in terms of solid)

Example A10

The same method as in Example A1 was conducted except that the thicknessratio of (layer A)/(layer B) was changed as shown in the table to give apolyester film for sealing the backside of solar cell having 50 μmthickness.

Example A11

The same method as in Example A1 was conducted except that a mixture of65% by mass of polyethylene terephthalate resin (PET-VI) and 35% by massof MB-VI was used as a material for the layer A and that a mixture of85% by mass of PET-VI, 7% by mass of MB-VI and 8% by mass of MB-V wasused as a material for the layer B to give a polyester film for sealingthe backside of solar cell having 50 μm thickness.

Example A12

The same method as in Example A1 was conducted except that a mixture of65% by mass of polyethylene terephthalate resin (PET-VII) and 35% bymass of MB-II was used as a material for the layer A and that a mixtureof 85% by mass of PET-VII, 7% by mass of MB-II and 8% by mass of MB-Vwas used as a material for the layer B to give a polyester film forsealing the backside of solar cell having 50 μm thickness.

Comparative Example A1

The same method as in Example A1 was used for conducting the stretchexcept that 100% by mass of polyethylene terephthalate resin (PET-II)was used for both layers A and B to give a polyester film for sealingthe backside of solar cell having 50 μm thickness.

Comparative Example A2

The same method as in Example A1 was used for conducting the stretchexcept that a mixture of 65% by mass of polyethylene terephthalate resin(PET-III) and 35% by mass of the previously prepared MB-I was used as amaterial for the layer A while a mixture of 85% by mass of PET-III, 7%by mass of MB-1 and 8% by mass of MB-V was used as a material for thelayer B and that both were poured into different extruders to give apolyester film for sealing the backside of solar cell having 50 μmthickness.

Comparative Example A3

The same method as in Example A1 was used except that a mixture of 65%by mass of polyethylene terephthalate resin (PET-III) and 35% by mass ofMB-II was used as a material for the layer A while a mixture of 85% bymass of PET-III, 7% by mass of MB-II and 8% by mass of MB-V was used asa material for the layer B to give a polyester film for sealing thebackside of solar cell having 50 μm thickness.

Comparative Example A4

The same method as in Example A1 was used except that a mixture of 65%by mass of polyethylene terephthalate resin (PET-VIII) and 35% by massof MB-II was used as a material for the layer A while a mixture of 85%by mass of PET-VIII, 7% by mass of MB-II and 8% by mass of MB-V was usedas a material for the layer B to give a polyester film for sealing thebackside of solar cell having 50 μm thickness.

TABLE 1 Example Example Example Example Example Example Example ExampleA1 A2 A3 A4 A5 A6 A7 A8 material layer A polyester material name PET-IIPET-II PET-II PET-II PET-II PET-II PET-V PET-II limiting viscosity 0.710.71 0.71 0.71 0.71 0.71 0.73 0.71 rate 65 65 65 65 65 65 65 65 Ti-M.Bmaterial name M.B-II M.B-II M.B-II M.B-II M.B-II M.B-II MB-IV M.B-IIlimiting viscosity 0.71 0.71 0.71 0.71 0.71 0.71 0.70 0.71 rate 35 35 3535 35 35 35 35 layer B polyester material name PET-II PET-II PET-IIPET-II PET-II PET-II PET-V PET-II limiting viscosity 0.71 0.71 0.71 0.710.71 0.71 0.73 0.71 rate 85 85 85 85 85 85 85 85 fine particles MBmaterial name M.B-II M.B-II M.B-II M.B-II M.B-II M.B-II MB-IV M.B-IIlimiting viscosity 0.71 0.71 0.71 0.71 0.71 0.71 0.70 0.71 rate 7 7 7 77 7 7 7 cavity-forming MB material name MB-V MB-V MB-V MB-V MB-V MB-VMB-V MB-V rate 8 8 8 8 8 8 8 8 film properties layering thickness μm3/44/3 8/109/8 11/166/11 3/44/3 3/44/3 3/44/3 3/44/3 3/44/3 (A/B/A)limiting viscosity dL/g 0.7 0.7 0.7 0.7 0.7 0.7 0.7 0.7 apparentspecific g/cm³ 1.12 1.12 1.11 1.04 0.9 1.13 1.12 1.12 gravity degree ofwhiteness — 94 95 96 94 94 94 94 94 acid value eq/ton 21 22 24 21 23 2214 21 content of % by mass 5.2 5.3 5.1 5.2 5.2 5.2 5.2 5.2 inorganicfine particles resistance to hydrolysis % 84 81 79 88 85 85 94 84retaining rate of elongation resistance to light % 61 80 95 61 62 60 6261 retaining rate of elongation layered numbers numbers 14 37 51 16 2014 14 14 of the cavities void layering density numbers/μm 0.28 0.3 0.270.32 0.4 0.28 0.28 0.28 MD HS150 % 2.5 2.4 2.3 2.6 2.4 0.4 2.6 2.5 MOR-C— 1.66 1.62 1.58 1.52 1.65 1.62 1.64 1.66 partial discharge V 605 9251220 615 620 610 610 605 voltage light reflectance % 84 86 88 85 87 8785 84 variation of the % 2 1 2 2 1 1 3 2 light reflectance DEG molar %1.6 1.6 1.6 1.6 1.6 1.6 1.6 1.6 strength of backside — ○ ○ ○ ○ ○ ○ ○ ○strength upon — ○ ○ ○ ○ ○ ○ ○ ○ processing surface flatness — ○ ○ ○ ○ ○○ ○ ○ Example Example Example Example Comparative ComparativeComparative Comparative A9 A10 A11 A12 Example A1 Example A2 Example A3Example A4 material layer A polyester material name PET-II — PET-VIPET-VII PET-II PET-III PET-III PET-VIII limiting viscosity 0.71 0.790.69 0.71 0.51 0.51 1.01 rate 65 65 65 100 65 65 65 Ti-M.B material nameM.B-II — MB-VI MB-II — M.B-I MB-II MB-II limiting viscosity 0.71 0.800.71 0.45 0.71 0.71 rate 35 35 35 35 35 35 layer B polyester materialname PET-II PET-II PET-VI PET-VIII PET-II PET-III PET-III PET-VIIIlimiting viscosity 0.71 0.71 0.79 0.69 0.71 0.51 0.51 1.01 rate 85 85 8585 100 85 85 85 fine particles MB material name M.B-II M.B-II MB-VIMB-II — M.B-I MB-II MB-II limiting viscosity 0.71 0.71 0.80 0.71 0.450.71 0.71 rate 7 7 7 7 7 7 7 cavity-forming MB material name MB-V MB-VMB-V MB-V — MB-V MB-V MB-V rate 8 8 8 8 8 8 8 film properties layeringthickness μm 3/44/3 0/50/0 3/44/3 3/44/3 3/44/3 3/44/3 3/44/3 3/44/3(A/B/A) limiting viscosity dL/g 0.7 0.7 0.76 0.66 0.71 0.47 0.51 0.85apparent specific g/cm³ 1.12 1 1.12 1.12 1.4 1.09 1.19 1.13 gravitydegree of whiteness — 94 88 94 94 — 93 93 92 acid value eq/ton 21 20 1922 6 51 48 19 content of inorganic % by mass 5.2 3.5 5.2 5.2 0 5.2 5.25.2 fine particles resistance to hydrolysis % 84 82 86 79 81 13 17 87retaining rate of elongation resistance to light % 61 52 61 61 20 62 6061 retaining rate of elongation layered numbers numbers 14 17 14 14 0 1615 16 of the cavities void layering density numbers/μm 0.28 0.34 0.280.28 0 0.32 0.3 0.32 MD HS150 % 2.5 2.1 2.5 2.5 2.5 2.3 2 2.5 MOR-C —1.66 1.54 1.66 1.66 1.66 1.51 1.5 1.6 partial discharge V 605 650 605605 490 620 610 620 voltage light reflectance % 83 80 84 85 12 75 78 80variation of the % 1 3 4 2 — 4 8 9 light reflectance DEG molar % 1.6 1.61.6 1.6 1.6 1.6 1.6 1.6 strength of backside — ○ x ○ ○ ○ ○ ○ ○ strengthupon — ○ ○ ○ ○ ○ ○ ○ ○ processing surface flatness — ○ ○ ○ ○ ○ ○ ○ ○

Example B1 Preparation of Film

A mixture of 60% by mass of polyethylene terephthalate resin (PET-II)and 40% by mass of the previously-prepared MB-II was used as materialsfor a layer A and a layer B. Each of them was poured into separateextruder, mixed and melted at 285° C. and conjugated in a melted stateso as to give A/B layers by using a feed-block. At that time, the rateof extruding amounts for the layer A to the layer B was controlled usinga gear pump. After that, the above was extruded using a T-die onto acooling drum adjusted to 30° C. whereupon a non-stretched sheet wasprepared.

(Preparation of Biaxially Stretched Film)

The resulting non-stretched sheet was uniformly heated at 75° C. using aheating roll and subjected to a roll stretch of 3.3 times by heating at100° C. using a non-contacting heater. The resulting uniaxiallystretched film was introduced to a tenter, subjected to a transversestretch of 4.0 times by heating at 140° C., subjected to a heatingtreatment at 215° C. for 5 seconds by fixing its width and furthersubjected to a 4% relaxation treatment at 210° C. in a widthwisedirection so as to give a substantially single-layered polyester filmfor sealing the backside of solar cell having 80 μm thickness (A/B=16/64μm).

Example B2

A mixture of 64% by mass of polyethylene terephthalate resin (PET-II)and 36% by mass of the previously-prepared MB-II was used as a materialfor a layer A while a mixture of 96% by mass of PET-II and 4% by mass ofMB-II was used as a material for a layer B. Each of them was poured intoseparate extruder, mixed and melted at 285° C. and conjugated in amelted state so as to give A/B layers by using a feed-block. At thattime, the rate of extruding amounts for the layer A to the layer B wascontrolled using a gear pump. After that, the above was extruded using aT-die onto a cooling drum adjusted to 30° C. whereupon a non-stretchedsheet was prepared. Preparation of a biaxially stretched film wasconducted by the same method as in Example B1 to give a polyester filmfor sealing the backside of solar cell having 80 μm thickness (A/B=16/64μm) comprising two kinds in two layers.

Example B3

The same method as in Example B2 was conducted except that PET-II in thelayers A and B was changed to PET-V and that MB-II was changed to MB-IVto give a polyester film for sealing the backside of solar cellcomprising two kinds in two layers.

Example B4

A mixture of 64% by mass of polyethylene terephthalate resin (PET-II)and 36% by mass of the previously-prepared MB-II was used as materialsfor a layer A and a layer B while a mixture of 56% by mass of PET-II,36% by mass of MB-II and 8% by mass of MB-V was used as a material for alayer B. Each of them was poured into separate extruder, mixed andmelted at 285° C. and conjugated in a melted state so as to give A/Blayers by using a feed-block. At that time, the rate of extrudingamounts for the layer A to the layer B was controlled using a gear pump.After that, the above was extruded using a T-die onto a cooling drumadjusted to 30° C. whereupon a non-stretched sheet was prepared.Preparation of a biaxially stretched film was conducted by the samemethod as in Example B1 to give a polyester film for sealing thebackside of solar cell having 50 μm thickness (A/B=10/40 μm) comprisingtwo kinds in two layers.

Example B5

The same method as in Example B4 was conducted except that PET-II in thelayers A and B was changed to PET-V and that MB-II was changed to MB-IVto give a polyester film for sealing the backside of solar cellcomprising two kinds in two layers.

Example B6 Manufacture of Master Batch Containing Fine Particles

As a material, a mixture of 50% by mass of a polyethylene terephthalateresin previously dried at 120° C. in 10⁻³ torr for about 8 hours with50% by mass of rutile-type titanium dioxide having an average particlesize of 0.3 μm (according to an electron microscopic method) wassupplied to a biaxial vent-type extruder, kneaded for 20 minutes,continuously sucked at 0.1 MPa and extruded at 275° C. together withdeaeration to prepare master bath (MB-VII) pellets containing fineparticles of rutile-type titanium dioxide. Limiting viscosity of theMB-VII was 0.48 dL/g. Acid value of the MB-VII was 39.8 eq/ton.

Further, solid-phase polymerization was conducted from the MB-VIIpellets in vacuo (10 Pa) until the limiting viscosity reached 0.75 dL/gto prepare a master batch (MB-VIII) containing fine particles ofrutile-type titanium dioxide. Acid value of MB-VIII was 10.1 eq/ton.

Manufacture of Polyethylene Terephthalate Resin (PET-IX)

Solid-phase polymerization was conducted from polyethylene terephthalateresin (PET-IV) using a rotary vacuum polymerization reactor underreduced pressure of 0.5 mmHg at 220° C. for different reaction time toprepare a polyethylene terephthalate resin (PET-IX) having limitingviscosity of 0.75 dL/g and acid value of 5.0 eq/ton.

(Preparation of Film)

Then, a mixture of 80% by mass of PET-IX and 20% by mass of thepreviously-prepared MB-VIII was used as a material for a layer A while amixture of 80% by mass of PET-IX, 12% by mass of MB-VIII and 8% by massof MB-V was used as a material for a layer B. Each of them was pouredinto separate extruder, mixed and melted at 280° C. and the layer B wasconjugated to one side of the layer A in a melted state by using afeed-block. At that time, the rate of extruding amounts for the layer Ato the layer B was controlled using a gear pump. After that, the abovewas extruded using a T-die onto a cooling drum adjusted to 30° C.whereupon a non-stretched sheet was prepared so as to give A/B/A layers.

(Preparation of Biaxially Stretched Film)

The resulting non-stretched sheet was uniformly heated at 70° C. using aheating roll and subjected to a roll stretch of 3.3 times at 90° C. Theresulting uniaxially stretched film was introduced to a tenter,subjected to a transverse stretch of 3.7 times by heating at 140° C.,subjected to a heating treatment at 220° C. for 5 seconds by fixing itswidth and further subjected to a 4% relaxation treatment at 220° C. in awidthwise direction. Both ends were trimmed, the resulting one was woundusing a winding apparatus and slit by dividing into equal two parts in awidthwise direction to give a roll of polyester film for sealing thebackside of solar cell having 1300 mm width, 3000 m length and 188 μmthickness (19/150/19).

TABLE 2 Example B1 Example B2 Example B3 Example B4 Example B5 ExampleB6 material layer A polyester material name PET-II PET-II PET-V PET-IIPET-V PET-IX limiting viscosity 0.71 0.71 0.73 0.71 0.73 0.75 rate 60 6464 64 50 80 Ti-M.B material name M.B-II M.B-II M.B-IV M.B-II M.B-IVM.B-VIII limiting viscosity 0.71 0.71 0.7 0.71 0.7 0.75 rate 40 36 36 3650 20 layer B polyester material name PET-II PET-II PET-V PET-II PET-VPET-IX limiting viscosity 0.71 0.71 0.73 0.71 0.73 0.75 rate 60 96 96 5656 80 fine particles MB material name M.B-II M.B-II M.B-IV M.B-II M.B-IVM.B-VIII limiting viscosity 0.71 0.71 0.7 0.71 0.7 0.75 rate 40 4 4 3636 12 cavity-forming MB material name MB-V MB-V MB-V rate 8 8 8 filmproperties layering thickness (A/B/A) μm 16/64/— 16/64 16/64 10/40/—10/40/— 19/150/19 limiting viscosity dL/g 0.65 0.68 0.71 0.68 0.7 0.78apparent specific gravity g/cm³ 1.42 1.41 1.41 1.15 1.12 1.07 degree ofwhiteness — 90 91 91 93 94 93 acid value eq/ton 29 21 17 25 21 6.9content of inorganic fine % by mass 20 5.2 5.2 18 18 6.8 particlesresistance to hydrolysis % 74 88 92 76 86 92 retaining rate ofelongation resistance to light % 78 66 66 76 76 40 retaining rate ofelongation layered numbers of the cavities numbers — — — 50 50 52 voidlayering density numbers/μm — — — 0.25 0.25 0.28 MD HS150 % 2.4 2.3 2.42.4 2.3 2.1 MOR-C — 1.67 1.6 1.58 1.58 1.52 1.57 partial dischargevoltage V 580 578 580 630 620 1240 light reflectance % 75 72 71 82 83 88variation of the light reflectance % 2 2 1 2 2 1 DEG molar % 1.5 1.6 1.61.6 1.6 1.6 strength of backside — ○ ○ ○ ○ ○ ○ strength upon processing— ○ ○ ○ ○ ○ ○ surface flatness — ○ ○ ○ ○ ○ ○

INDUSTRIAL APPLICABILITY

The polyester film for sealing the backside of solar cell according tothe present invention is excellent in light reflectivity and durabilityand is also excellent in electric insulation whereby it is useful as asheet for protective sealing of the backside of solar cell.

1. A polyester film for sealing the backside of a solar cell, whichpolyester film has a light reflectance at 550 nm wavelength of 50% ormore, contains 3 to 50% by mass of inorganic fine particles, has an acidvalue of 1 to 30 eq/ton, and has a limiting viscosity of 0.60 to 0.80dL/g.
 2. The polyester film for sealing the backside of a solar cellaccording to claim 1, wherein in-face variation of the light reflectanceto the mean value of the light reflectance is 5% or less.
 3. Thepolyester film for sealing the backside of a solar cell according toclaim 1, wherein the inorganic fine particles are titanium oxide of arutile type.
 4. The polyester film for sealing the backside of a solarcell according to claim 1, wherein the polyester film has a thickness of30 to 300 μm.
 5. The polyester film for sealing the backside of a solarcell according to claim 1, wherein the polyester film has a partialdischarge voltage of 550 V or higher.
 6. The polyester film for sealingthe backside of a solar cell according to claim 1, wherein the layerednumbers of cavities existing in the thickness direction of the film is 5or more and the density of layered numbers of cavities defined by thefollowing formula is within a range of 0.1 to 7/μm:Density of layered numbers of cavities (numbers/μm)=[Layered numbers ofcavities in the thickness direction of film (numbers)]/[Thickness offilm (μm)].
 7. The polyester film for sealing the backside of a solarcell according to claim 1, wherein an applied layer is provided at leaston one side of the film, wherein a urethane resin is a main component ofthe applied layer, and wherein an aliphatic polycarbonate polyol is aconstituting component of the urethane resin.
 8. The polyester film forsealing the backside of a solar cell according to claim 1, wherein thefilm is used on the face of a side contacting an encapsulation foil fora solar cell module and/or on the outermost face of a solar cell module.9. The polyester film for sealing the backside of a solar cell accordingto claim 1, wherein the film is obtained by preparing a master batchcomprising a polyester resin and inorganic fine particles; subjectingthe master batch to solid-phase polymerization and; after that, pouringa polyester resin containing no inorganic fine particles and the masterbatch into an extruder and melt extruding the mixture.
 10. A solar cellmodule containing the polyester film for sealing the backside of a solarcell according to claim 1, wherein an encapsulation foil layer isadjacent to the polyester film and a solar cell device is embedded inthe encapsulation foil layer.
 11. The polyester film for sealing thebackside of a solar cell according to claim 1, wherein in-face variationof the light reflectance to the mean value of the light reflectance is5% or less, the inorganic fine particles are titanium oxide of a rutiletype, the polyester film has a thickness of 30 to 300 μm, and thepolyester film has a partial discharge voltage of 550 V or higher. 12.The polyester film for sealing the backside of a solar cell according toclaim 11, wherein the layered numbers of cavities existing in thethickness direction of the film is 5 or more and the density of layerednumbers of cavities defined by the following formula is within a rangeof 0.1 to 7/μm:Density of layered numbers of cavities (numbers/μm)=[Layered numbers ofcavities in the thickness direction of film (numbers)]/[Thickness offilm (μm)].
 13. The polyester film for sealing the backside of a solarcell according to claim 12, wherein an applied layer is provided atleast on one side of the film, wherein a urethane resin is a maincomponent of the applied layer, and wherein an aliphatic polycarbonatepolyol is a constituting component of the urethane resin.
 14. A solarcell module containing the polyester film for sealing the backside of asolar cell according to claim 11, wherein an encapsulation foil layer isadjacent to the polyester film and a solar cell device is embedded inthe encapsulation foil layer.
 15. A solar cell module containing thepolyester film for sealing the backside of a solar cell according toclaim 12, wherein an encapsulation foil layer is adjacent to thepolyester film and a solar cell device is embedded in the encapsulationfoil layer.
 16. A solar cell module containing the polyester film forsealing the backside of a solar cell according to claim 13, wherein anencapsulation foil layer is adjacent to the polyester film and a solarcell device is embedded in the encapsulation foil layer.